430S17, F2281 430, F593 430, F738 430, BS2320, 1.4016, 430, S43000, X6CR17
430 Stainless Steel Threaded Rod are martensitic stainless steel threaded rod manufactured from alloy containing chromium and nickel. Stainless Steel 430 threaded rod are used for corrosive environments. TorqBolt is an eminent 430 stainless steel threaded rod supplier in India.
430 Stainless Steel Bolts Type 430 Stainless Steel Fasteners 430 Stainless Steel Forgings Type 430 Stainless Nuts SS 430 Screws 430 Stainless Steel Threaded Rod Type 430 Stainless Washers 1.4016 Screws
Type Of Steel/Alloy | Grade | Steel Number | Steel Designation | UNS | Trade Name |
---|---|---|---|---|---|
Ferritic | F1 | 1.4016 | X6Cr17 | S43000 | 430 |
Stainless steel grade | Chemical composition a (cast analysis, mass fractionin %) b | Other elements and notes | ||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|
C | Si | Mn | P | S | Cr | Mo | Ni | Cu | N | |||
Ferritic | F1 | 0,08 | 1,00 | 1,00 | 0,040 | 0,030 | 15,0 to 18,0 | _ f | 1,00 | - | - | j |
Stainless steel grade | Property class | Tensile strength a Rmf min. MPa | Stress at 0,2 % non-proportional elongation b Rpf mm. MPa | Elongation after fracture A min. mm | ||||
---|---|---|---|---|---|---|---|---|
Ferritic | F1d | 45 | 450 | 250 | 0,2d | 135 to 220 | - | 128 to 209 |
60 | 600 | 410 | 0,2d | 180 to 285 | - | 171 to 271 |
Stainless steel grade | Property and related test method | |||||
---|---|---|---|---|---|---|
Minimum tensile strength Rmr | Stress at 0,2 % non-proportional elongation Rpf | Elongation after fracture A | Minimum breaking torque M B | Hardness | ||
Tensile test 9.1 | Wedge tensile test 9.4 | Tensile test 9.1 | Tensile test 9.1 | Torsional test 9.5 | Hardness test 9.6 | |
F1 | d ≥ 3 mm I ≥ 2,Sd b ≥ 2d | Not relevant | d ≥ 3 mm I ≥ 2,Sd b ≥ 2d | d ≥ 3 mm I ≥ 2,Sd b ≥ 2d | No value available | Applicable |
Stainless steel grade | Property and related test method | ||||
---|---|---|---|---|---|
Minimum tensile strength Rmr | Stress at 0,2 % non-proportional elongation Rpf | Elongation after fracture A | Minimum tensile load Fmr | Hardness | |
Tensile test 9.1, 9.3 | Tensile test 9.1 | Tensile test 9.1 | Tensile test 9.2 | Hardness test 9.6 | |
F1 | d ≥ 3 mm for all lengths, when b ≥ 3d a | d ≥ 3 mm for all lengths | Applicable |