430S17, F2281 430, F593 430, F738 430, BS2320, 1.4016, 430, S43000, X6CR17
430 Stainless Steel Screws are martensitic stainless steel screw manufactured from alloy containing chromium and nickel. Stainless Steel 430 Set Screw are used for corrosive environments. TorqBolt is an eminent 430 stainless steel screw supplier in India.
Type 430 Stainless Steel Bolts Type 430 Stainless Steel Fasteners Type 430 Stainless Forgings SS 430 Nuts 430 Stainless Steel Machine Screws Type 430 Stainless Steel Threaded Rod 430 Stainless Steel Washers 1.4016 Nuts
Type Of Steel/Alloy | Grade | Steel Number | Steel Designation | UNS | Trade Name |
---|---|---|---|---|---|
Ferritic | F1 | 1.4016 | X6Cr17 | S43000 | 430 |
Stainless steel grade | Chemical composition a (cast analysis, mass fractionin %) b | Other elements and notes | ||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|
C | Si | Mn | P | S | Cr | Mo | Ni | Cu | N | |||
Ferritic | F1 | 0,08 | 1,00 | 1,00 | 0,040 | 0,030 | 15,0 to 18,0 | _ f | 1,00 | - | - | j |
Stainless steel grade | Property class | Tensile strength a Rmf min. MPa | Stress at 0,2 % non-proportional elongation b Rpf mm. MPa | Elongation after fracture A min. mm | ||||
---|---|---|---|---|---|---|---|---|
Ferritic | F1d | 45 | 450 | 250 | 0,2d | 135 to 220 | - | 128 to 209 |
60 | 600 | 410 | 0,2d | 180 to 285 | - | 171 to 271 |
Stainless steel grade | Property and related test method | |||||
---|---|---|---|---|---|---|
Minimum tensile strength Rmr | Stress at 0,2 % non-proportional elongation Rpf | Elongation after fracture A | Minimum breaking torque M B | Hardness | ||
Tensile test 9.1 | Wedge tensile test 9.4 | Tensile test 9.1 | Tensile test 9.1 | Torsional test 9.5 | Hardness test 9.6 | |
F1 | d ≥ 3 mm I ≥ 2,Sd b ≥ 2d | Not relevant | d ≥ 3 mm I ≥ 2,Sd b ≥ 2d | d ≥ 3 mm I ≥ 2,Sd b ≥ 2d | No value available | Applicable |
Stainless steel grade | Property and related test method | ||||
---|---|---|---|---|---|
Minimum tensile strength Rmr | Stress at 0,2 % non-proportional elongation Rpf | Elongation after fracture A | Minimum tensile load Fmr | Hardness | |
Tensile test 9.1, 9.3 | Tensile test 9.1 | Tensile test 9.1 | Tensile test 9.2 | Hardness test 9.6 | |
F1 | d ≥ 3 mm for all lengths, when b ≥ 3d a | d ≥ 3 mm for all lengths | Applicable |