420S37, BS2303, 1.4021, 420J1, S42000, X20CR13
420 Stainless Steel Nuts are martensitic stainless steel nuts manufactured from alloy containing chromium and nickel. Stainless Steel 420 Nuts are used for corrosive environments. TorqBolt is an eminent 420 stainless steel nuts supplier in India.
420 Stainless Steel Bolts 420 Stainless Fasteners Type 420 Stainless Steel Rings SS 420 Nuts 420 Stainless Steel Screws SS 420 Threaded Rod 420 Stainless Washers 1.4021 Bolts
Type Of Steel/Alloy | Grade | Steel Number | Steel Designation | UNS | Trade Name |
---|---|---|---|---|---|
General purpose martensitic | C1 | 1.4021 | X20Cr13 | S42000 | 420 |
Stainless steel grade | Chemical composition a (cast analysis, mass fractionin %) b | Other elements and notes | ||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|
C | Si | Mn | P | S | Cr | Mo | Ni | Cu | N | |||
Martensitic | C1 | 0,09 to 0,15 | 1,00 | 1,00 | 0,050 | 0,030 | 11,5 to 14,0 | - | 1,00 | - | - | i |
Stainless steel grade | Property class | Tensile strength a Rmr min. MPa | Stress at 0,2 % non-proportional elongation b Rpr mm. MPa | Elongation after fracture A min. mm | Hardness min. to max. | |||
---|---|---|---|---|---|---|---|---|
HV | HRC | HBW | ||||||
Martensitic | C1 | 50 | 500 | 250 | 0,2d | 155 to 220 | - | 147 to 209 |
70 | 700 | 410 | 0,2d | 220 to 330 | 20 to 34 | 209 to 314 | ||
110 c | 1100 | 820 | 0,2d | 350 to 440 | 36 to 45 | - |
Stainless steel grade | Property and related test method | |||||
---|---|---|---|---|---|---|
Minimum tensile strength Rmr | Stress at 0,2 % non-proportional elongation Rpf | Elongation after fracture A | Minimum breaking torque M B | Hardness | ||
Tensile test 9.1 | Wedge tensile test 9.4 | Tensile test 9.1 | Tensile test 9.1 | Torsional test 9.5 | Hardness test 9.6 | |
C1 | d ≥ 3 mm I ≥ 2,Sd b ≥ 2d | d ≥ 3 mm I ≥ 2,Sd b ≥ 2d | d ≥ 3 mm I ≥ 2,Sd b ≥ 2d | d ≥ 3 mm I ≥ 2,Sd b ≥ 2d | No value available | Applicable |
Stainless steel grade | Property and related test method | ||||
---|---|---|---|---|---|
Minimum tensile strength Rmr | Stress at 0,2 % non-proportional elongation Rpf | Elongation after fracture A | Minimum tensile load Fmr | Hardness | |
Tensile test 9.1, 9.3 | Tensile test 9.1 | Tensile test 9.1 | Tensile test 9.2 | Hardness test 9.6 | |
C1 C3 C4 | d ≥ 3 mm for all lengths, when b ≥ 3d a | d ≥ 3 mm for all lengths | Applicable |